Table 2 Ultimate tensile strength and yield strength of the 6061 aluminum alloy Full size table According to ASTM B209-14: Standard Specification for Aluminum
We are more than an aluminium alloy solution provider.
Do you need consumer aluminium alloy products or learn more info about aluminum alloy prices?
Table 2 Ultimate tensile strength and yield strength of the 6061 aluminum alloy Full size table According to ASTM B209-14: Standard Specification for Aluminum
Brief introduction to 6xxx wrought aluminum alloys. Tabular data of yield strength, tensile strength, elongation, and modulus of elasticity, at elevated temperatures and at room
General 6061 characteristics and uses: Excellent joining characteristics, good acceptance of applied coatings. Combines relatively high strength, good workability, and high
6061 ，6XXX 。. ，。.
The shear strength of 6061 aluminum alloy is 207 MPa (30000 psi), and these values are summarized in Table 1. Fatigue strength is the ability of a material to resist
Figure 1.5.3.3 Quench sensitivity of 6061 alloy compared with other heat treatable aluminum alloys: (a) yield strength after aging to designated temper; (b) tensile
Surface Emissivity Coefficients The radiation heat transfer emissivity coefficients for some common materials like aluminum, brass, glass and many more. Young\'s Modulus,
Group: Heat Treatable Alloys ALUMINUM ALLOY 6061 GENERAL DESCRIPTION: The combination of magnesium and silicon in 6061 aluminum allows it to be heat treated to
T6 temper 6061 has been treated to provide the maximum precipitation hardening (and therefore maximum yield strength) for a 6061 aluminium alloy. It has an ultimate tensile strength of at least 290 MPa (42 ksi) and yield strength of at least 240 MPa (35 ksi). More typical values are 310 MPa (45 ksi) and 270 MPa (39 ksi), respectively.
Table 2 Ultimate tensile strength and yield strength of the 6061 aluminum alloy Full size table According to ASTM B209-14: Standard Specification for Aluminum and Aluminum Alloy Sheet and Plate, the minimum yield and ultimate tensile strength must be higher than 85 MPa and 205 MPa for T4
Brief introduction to 6xxx wrought aluminum alloys. Tabular data of yield strength, tensile strength, elongation, and modulus of elasticity, at elevated temperatures and at room temperature after heating. Creep, creep
General 6061 characteristics and uses: Excellent joining characteristics, good acceptance of applied coatings. Combines relatively high strength, good workability, and high resistance to corrosion; widely available. The T8 and T9 tempers
Aluminum 6061-T6 has a minimum yield strength of 35 ksi (240 MPa), which is almost equal to that of A36 steel. This strength, combined with its light weight (about 1/3 that of steel), makes it particularly suitable for structural applications where static loads are a
6061 ，6XXX 。. ，。. 。. ， 6061-O, 6061-T4, 6061-T6, 6061-T651, 6061-T42
The shear strength of 6061 aluminum alloy is 207 MPa (30000 psi), and these values are summarized in Table 1. Fatigue strength is the ability of a material to resist breaking under cyclical loading, where a small load
Figure 1.5.3.3 Quench sensitivity of 6061 alloy compared with other heat treatable aluminum alloys: (a) yield strength after aging to designated temper; (b) tensile strength after aging to designated temper (Ref.
Surface Emissivity Coefficients The radiation heat transfer emissivity coefficients for some common like aluminum, brass, glass and many more. Young\'s Modulus, Tensile Strength and Yield Strength Values for some
Group: Heat Treatable Alloys ALUMINUM ALLOY 6061 GENERAL DESCRIPTION: The combination of magnesium and silicon in 6061 aluminum allows it to be heat treated to higher strength levels. It has good formability when in the fully soft, annealed condition and the strength can be significantly increased following a heat treatment. What is 6061